TU 6-10-2002-85
Film Color: cyan RAL 6033, gray RAL 7000, gray RAL 7001, light gray, light blue, blue gray, gray turquoise, beige, yellow RAL 1004, orange, black.
Type: suspension of pigments in the solution of copolymer of vinyl chloride and vinyl acetate in the blend of organic solvents with addition of epoxy resin, plasticizer and corrosion inhibitor.
Sphere of application: it is intended for providing the corrosion protection of external surfaces of equipment, metal and reinforced-concrete structures and pipelines under conditions of the industrial atmosphere of chemical productions exposed to salts, aggressive gases and other chemical agents with the temperature of not above 60°С.
Properties: it forms chemically resistant coating. The film is smooth, uniform, free of sags and foreign inclusions.
Surface preparation: the surface to be painted shall be cleaned from loose rust and loose coating, and degreased. The compound shall be applied not later than after 6 hours from the moment of preparation of the surface.
Coating application: prior to application, hardener No.5 (TU 6-10-1093) shall be added to the semimanufactured product in the following mass proportion: 2.6 weight parts of hardener No.5 shall be taken per 100 weight parts of the semimanufactured compound. The compound shall be diluted to the working viscosity with the R-4 or R-4A solvent as per GOST 7827. In case of application by means of a roller or brush, the compound shall be applied without dilution.
The consumption per layer of the coating with the thickness of 25 μm is 130 to 160 g/m2.
Safety precautions: when performing the painting works as well as after finishing them, it is necessary to ventilate the room thoroughly. Use rubber gloves to protect your hands. Keep the enamel in a tightly closed container ensuring the protection against moisture and direct sunlight.
Keep away from fire!